Description
By incorporating German-imported organic impregnated short-cut carbon fibers into PLA, we have enhanced the strength and modulus of the material. The addition of carbon fibers not only reinforces the PLA but also provides it with a matte appearance and a distinctive carbon fiber sandblasted texture.
Whether used as structural components or for aesthetic purposes, ePLA-CF effortlessly excels, thanks to its outstanding attributes. Its printing performance is exceptional, making it suitable for high-speed printing.
Features
High strength
Matte appearance
Carbon fiber frosted texture
Excellent printability
High speed printing
Vacuumed Sealed Packaging
Notes
1.If there is a decrease in printing performance with ePLA-CF, it is recommended to pre-dry (40°C/ >4H) before printing to achieve the best printing results. During printing, it is advised to use it in conjunction with filament dryer box.
2.ePLA-CF filament is relatively rigid and should not be excessively bent. In the feeding pipeline, try to avoid excessive bending of the filament to prevent breakage.
3.ePLA-CF contains carbon fiber, and prolonged use may cause excessive wear on the nozzle and extruder gears. It is recommended to use a hardened steel nozzle or a ruby nozzle, and if possible, opt for hardened steel extruder gears.
Specifications
Model: eSun ePLA-CF
Diameter Format: 1.75mm
Net Weight: 1kg
Printing Temperature: 190-230℃ (Recommended to use hardened steel nozzle print at 215℃)
Bed Temperature: 45-60℃
Density: 1.21 g/cm3
Tensile Strength: 28 MPa
Elongation at Break: 90%
Flexural Strength: 77 MPa
Flexural Modulus: 3552 MPa
IZOD Impact Strength: 4.1 KJ/m²
Melt Flow Index (g/10min): 5.37(190℃/2.16kg)
Heat Distortion Temperature: 53 (℃, 0.45 MPa)
Tolerance: ±0.03mm
Certificate: TDS, MSDS
Packaging: Vacuum packed with silica desiccant
Warranty: 1 Year